In this study, copper nanoparticles (CuNP) were synthesized by chemical reduction of Cu 2+ with reducing agent NaHB 4 in a chitosan stabilizer. Characterization of CuNPs was performed using UV-Vis spectra, X-ray Diffraction (XRD) patterns and Transmission Electron Microscopy (TEM) images. The ability of CuNP to inhibit the growth of Fusarium oxysporum was investigated at concentrations between 20 and 100 ppm. The results showed that CuNP samples significantly inhibited the growth of Fusarium oxysporum, with smaller particle diameter exhibiting a higher antifungal effect. The 26.5 nm CuNPs displayed greater antifungal efficiency than the 29 nm CuNPs. Complete inhibition was observed at a concentration of >
80 ppm after 7 days of culture for the 2.0 CuNP (26.5 nm) sample, while the fungus remained viable on PDA plates containing 1.5 CuNPs (29 nm).Trong nghiên cứu này, nano đồng được tổng hợp bằng phương pháp khử hóa học Cu 2+ với chất khử NaHB 4 trong chất ổn định chitosan. Đặc tính của hạt nano đồng được xác định bằng phô UV-Vis, nhiễu xạ tia X (XRD) và kính hiển vi điện tử truyền qua (TEM). Hiệu quả kháng nấm của CuNP được đánh giá băng thử nghiệm chống nấm Fusarium oxysporum ở các nồng độ khác nhau từ 20 - 100 ppm. Kết quà cho thấy, các mẫu hạt nano đồng đã ức chế đáng kể sự phát triển của Fusarium oxysporum và đường kính hạt càng nhỏ thì hiệu quả kháng nấm càng cao. Các hạt nano đồng có kích thước 26,5 nm cho thấy hiệu quả kháng nấm cao hơn các hạt nano đồng 29 nm. Sự ức chế hoàn toàn được quan sát thấy ở nồng độ >
80 ppm sau 1 ngày và thậm chí 7 ngày nuôi cấy đối với mẫu 2.0 CuNP (26.5 nm), trong khi nấm vẫn tồn tại trên các đĩa PDA chứa 1.5 CuNP (29 nm).