Experimental Investigation of Crack Initiation in Face-Centered Cubic Materials in the High and Very High Cycle Fatigue Regime

 0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Thomas Straub

Ngôn ngữ: eng

ISBN-13: 978-3731504719

ISBN: KSP/1000051515

Ký hiệu phân loại: 620 Engineering and allied operations

Thông tin xuất bản: KIT Scientific Publishing 2016

Mô tả vật lý: 1 electronic resource (XXX, 185 p. p.)

Bộ sưu tập: Tài liệu truy cập mở

ID: 228717

This book investigates the fatigue mechanisms and crack initiation of Ni, Al and Cu on a small-scale in the Very High Cycle Fatigue regime by means of innovative fatigue experimentation. A novel custom-built resonant fatigue setup showed that the sample resonant frequency changes with increasing cycle number due to fatigue damage. Mechanisms such as slip band formation have been observed. Cyclic hardening, vacancy and oxidation formation may be considered as early fatigue mechanisms.
Tạo bộ sưu tập với mã QR

THƯ VIỆN - TRƯỜNG ĐẠI HỌC CÔNG NGHỆ TP.HCM

ĐT: (028) 71010608 | Email: tt.thuvien@hutech.edu.vn

Copyright @2024 THƯ VIỆN HUTECH