Chế tạo màng molybden disulfua trên thuỷ tinh phủ oxit thiếc pha tạp flo bằng phương pháp quét thế vòng tuần hoàn=The production of molybdenum disulfide film onto flourine - doped tin oxide coated glass by cyclic voltammetry method

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Nguyễn Trầm Yên Châu, Thị Thúy Lam Mai

Ngôn ngữ: vie

Ký hiệu phân loại:

Thông tin xuất bản: Tạp chí Công thương, 2024

Mô tả vật lý: tr.348-353

Bộ sưu tập: Metadata

ID: 244463

Thêm vào giỏ

Bài viết mô tả quá trình lắng đọng điện hóa tạo màng molybden disulfua (MoS 2 ) trên thuỷ tinh phủ oxit thiếc pha tạp flo (FTO) bằng phương pháp quét thế vòng tuần hoàn (CV) sử dụng tiền chất là amoni molybdate tetrahydrate và natri thiosulfate pentahydrate. Các thông số trong quá trình chế tạo màng đã được khảo sát gồm nồng độ và pH của dung dịch tạo màng, số chu kỳ và tốc độ quét thế. Các thông số này ảnh hưởng đến độ dày, hình thái và hoạt tính xúc tác điện hóa của màng MoS2. Kết quả cho thấy màng MoS 2 có hoạt tính xúc tác điện hoá cao nhất trong dung dịch ferrocene 5,0 mM, TBAP 0,1 M được điều chế từ dung dịch điện ly chứa (NH 4 ) 6 M o7 O 24 2,5 Mm, Na 2 S 2 O 3 1 mM và KC1 0,1 M (pH 6) sau 15 chu kỳ quét từ -1,0 V đến 1,0 V ở tốc độ quét 100 mV.S -1 Ngoài ra, đặc tính hình thái của màng MoS 2 sản phẩm còn được xác định bằng phương pháp kính hiển vi điện tử quét (SEM) và quang phổ Raman.This report outlines the electrochemical deposition of molybdenum disulfide (MoS 2 ) film onto fluorine - doped tin oxide coated glass (FTO) using the cyclic voltammetry method (CV) with precursors being ammonium molybdate tetrahydrate and sodium thiosulfate pentahydrate. Parameters in the electro-deposited experiment such as the concentration and pH of electrolyte solution, number of cycles, scanning rate were investigated. These parameters affect the thickness, morphology and electrocatalytic activity of the MoS 2 film. The resulting shows that MoS2 film exhibiting the highest electrocatalytic activity in 5.0 mM ferrocene, 0.1 M TBAP solution was prepared from an aqueous electrolyte containing 2.5 mM (NH 4 ) 6 M o7 O 24 , 1.0 mM Na 2 S 2 O 3 and 0.1 M KC1 (pH 6) after 15 cycles between -1.0 V to 1.0 V at a scanning rate of 100 mV.S -1 . Beside, the obtained MoS 2 film was characterized by Raman spectroscopy and scanning electron microscopy (SEM).

1. Đọc trực tuyến

1. Đọc trực tuyến

Tạo bộ sưu tập với mã QR