Si-based materials for lithium-ion batteries VI. 15% surface-modified Si/C-graphite/carbon black/lithiated polyacrylic acid electrode [electronic resource]

• Ngôn ngữ: eng
• Ký hiệu phân loại: 333.912 +Water for domestic and industrial uses
• Thông tin xuất bản: Washington, D.C. : Oak Ridge, Tenn. : United States. Dept. of Energy. Office of Energy Efficiency and Renewable Energy ; Distributed by the Office of Scientific and Technical Information, U.S. Dept. of Energy, 2020
• Mô tả vật lý: Size: Article No. 014013 : , digital, PDF file.
• Bộ sưu tập: Metadata
• ID: 257918
• Chủ đề: 1. 17 wind energy; 2. Energy storage; 3. Lithium-ion battery anode; 4. Silicon electrode

Tóm tắt

 X-ray photoelectron spectroscopy was used to analyze a 15%Si/C-graphite/carbon black/lithiated polyacrylic acid electrode fabricated at the Cell Analysis, Modeling, and Prototyping Facility (CAMP), Argonne National Laboratory. The spectra were obtained using incident monochromatic Al K<
 sub>
 ?<
 /sub>
  radiation at 1486.6 eV (0.83 401 nm). An initial survey spectrum together with O 1s, C 1s, and Si 2p are presented. A final survey spectrum was collected to ascertain the amount of beam-induced damage, which appears to be minimal. The spectra indicate the principal core level photoelectron and Auger electron signals with only minor nitrogen and lithium signals and show the expected silicon-carbon species related to the surface modification process in addition to oxidized carbon and silicon due to atmospheric exposure as well contributions related to the binder material.