Exfoliated graphite was synthesized by thermal microwave – assisted method. Here, we reported the facile synthesis and characterization of chemical bonds of EG using several techniques such as X-ray Power Diffraction Spectroscopy (XRD), Fourier-transform infrared spectroscopy (FT-IR), and and N2 adsorption/desorption isotherm mesurement. The result of XRD analysis showed peak intensity, proving the high crystallinity of EG, which is suitable with the FT-IR analysis. The specific surface area and pore volume of EG achieved were 40.95 m2/g and 0.16176 cm3/g, respectively. To elucidate the adsorption kinetic of CR over EG adsorbents, kinetic models including: pseudo first-order, pseudo second-order, Elovich, and Bangham models have been adopted. The kinetic results indicated that models adhered to the pseudo second-order equation with high coefficients R2 >
0.98.Vật liệu graphit tróc nở được tổng hợp bằng phương pháp chiếu xạ vi sóng. Cấu trúc vật liệu được đánh giá bằng các phương pháp phân tích nhiễu xạ tia X (XRD), quang phổ hồng ngoại chuyển đổi Fourier FT-IR và đẳng nhiệt hấp phụ - khử hấp phụ N2. Kết quả phân tích nhiễu xạ tia X cho cường độ peak, chứng tỏ graphit tróc nở (EG) được hình thành với độ tinh thể cao, phù hợp với kết quả phân tích phổ hồng ngoại chuyển đổi FT-IR. Diện tích bề mặt riêng của BET và thể tích lỗ rỗng của vật liệu EG được đo tương ứng là 40,95m2/g và 0,16176cm3/g. Đánh giá động học hấp phụ Congo Red thông qua các mô hình động học như: mô hình giả kiến bậc 1, mô hình giả kiến bậc 2, Elovich và Bangham trên EG chỉ ra sự hấp phụ CR lên EG tuân theo mô hình động học giả kiến bậc 2 với hệ số tương quan R2 >
0.98.