Currently, the demand for fabrics with water resistance is increasinglywidely used in clothing products in humid climates, sportswear and protectiveclothing,... The research creates Water-resistant woven fabrics are essential. Inthis paper, the influence of some structural parameters such as fabric weight(g/m2), yarn density (yarn/10cm) and fabric thickness (mm) has been presentedon the water resistance. of 3 samples of 100% polyester woven fabric, with thewater-resistant chemical used, TP-Phob FC 2904 combined with Phobol extenderxan crosslinker, CH3COOH acid and soft water with a solution with pH = 5.Research results show that the larger the weight (g/m2) and the thickness (mm)of the fabric, the higher the water resistance of the fabric (%). Research resultsare the scientific basis for manufacturers to choose fabric structure parameterssuitable for the use of water-resistant fabrics.Hiện nay, nhu cầu vải có khả năng kháng nước ngày càng được ứng dụngrộng rãi dùng trong các sản phẩm quần áo ở nơi có khí hậu ẩm ướt, quần áo thểthao và quần áo bảo vệ,... Việc nghiên cứu tạo ra những loại vải dệt thoi có khảnăng kháng nước là rất cần thiết. Trong bài báo này, đã trình bày nghiên cứu ảnhhưởng của một số thông số cấu trúc như khối lượng vải (g/m2), mật độ sợi(sợi/10cm) và độ dày của vải (mm) đến khả năng kháng nước của 3 mẫu vải dêtthoi 100% polyester, với hóa chất kháng nước được sử dụng là chất TP-Phob FC2904 kết hợp với chất liên kết ngang Phobol extender xan, axit CH3COOH và nướcmềm với dung dịch có độ pH = 5. Kết quả nghiên cứu cho thấy, khối lượng(g/m2) và độ dày (mm) của vải càng lớn thì độ kháng nước của vải (%) càng cao.Kết quả nghiên cứu là cơ sở khoa học để các nhà sản xuất lựa chọn thông số cấutrúc vải phù hợp với mục đích sử dụng của vải kháng nước.