Nghiên cứu thực nghiệm xác định sức kháng cắt còn lại của dầm bê tông cốt thép nhịp ngắn đã bị ăn mòn cốt đai

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Hữu Tài Đinh, Công Hậu Nguyễn, Huy Cường Nguyễn

Ngôn ngữ: vie

Ký hiệu phân loại:

Thông tin xuất bản: Tạp chí Khoa học và Công nghệ Việt Nam - B, 2022

Mô tả vật lý: tr.21

Bộ sưu tập: Metadata

ID: 329557

Thêm vào giỏ Liên kết toàn văn

Bài báo trình bày kết quả nghiên cứu thực nghiệm xác định sức kháng cắt còn lại của dầm bê tông cốt thép (BTCT) có cốt đai đã bị ăn mòn ở các mức độ khác nhau. Trong nghiên cứu này, có 10 dầm đã được thí nghiệm uốn 3 điểm, trong đó có 4 dầm được gia tốc quá trình ăn mòn cốt thép trong 60 và 80 ngày để đạt được mức độ mất mát khối lượng cốt thép đai lần lượt là 10 và 20%. Ứng xử chịu lực của dầm bao gồm quan hệ lực - độ võng, cấu trúc vết nứt, sức kháng cắt còn lại và dạng phá hoại sẽ được phân tích. So với các dầm đối chứng không bị ăn mòn, sức kháng cắt của các dầm bị ăn mòn suy giảm đến 16,08 và 25,34% tương ứng với mức độ ăn mòn theo khối lượng của cốt thép đai là 12,3 và 23,6%.This paper reports an experimental investigation on the residual shear strength of the corrodeị d RC beams with stirrups having different levels of corrosion. A total of ten beams was tested, including four beams were subjected to an electrochemically accelerated aging technique for 60 and 80 days to obtain the theoretical mass loss in their stirrups of 10% and 20%, respectively. The objective of the test program was to investigate the shear performances of strengthened beams loaded up to failure, including load-deflection behaviour, crack patterns, ultimate capacities, and modes of failure. Compared to the un-corroded specimens, the average shear strength of corroded specimens decreased by 16.08% and 25.34%, corresponding to the degree of corrosion of 12.3% and 23.6%.

1. Đọc trực tuyến

1. Đọc trực tuyến

Tạo bộ sưu tập với mã QR