Khảo sát thực nghiệm cơ tính và tổ chức tế vi của mối hàn giáp mối thép PERFORM 700 ứng dụng trong các kết cấu chịu lực cao

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: `Nguyễn Hồng Phong, Đức Mạnh Đinh, Xuân Hùng Lê, Vân Thương Lục, Ngọc Tân Nguyễn, Quốc Hoàng Phạm, Tuấn Anh Phùng

Ngôn ngữ: vie

Ký hiệu phân loại:

Thông tin xuất bản: Journal of Science and Technique, 2022

Mô tả vật lý: tr.53

Bộ sưu tập: Metadata

ID: 329637

Thêm vào giỏ Liên kết toàn văn

Bài báo trình bày kết quả nghiên cứu thực nghiệm công nghệ hàn giáp mối các tấm thép cường độ cao PERFORM 700 bằng dây hàn có lõi Kiswel K-110TK3 dưới lớp khí bảo vệ MAG. Tính hàn của vật liệu nền, sự thích ứng với dây hàn cũng như cơ tính của mối hàn được đánh giá bằng phương pháp kiểm tra chụp ảnh phóng xạ (RT), soi tổ chức tế vi kết cấu mối hàn và thử kéo, thử uốn mẫu hàn. Kết quả nghiên cứu chỉ ra rằng kim loại PERPORM 700 có tính hàn tốt, mối hàn chắc và ngấu, không ngậm xỉ, mối hàn khá dẻo dai, không xuất hiện vết nứt, rách. Cơ tính của mối hàn đạt giới hạn chảy và giới hạn bền kéo (712,0-720,0) MPa và (830,0-844,1) MPa. Kết quả nghiên cứu là cơ sở để ứng dụng thép PERPORM và dây hàn Kiswel K-110TK3 trong chế tạo các kết cấu yêu cầu chịu lực cao, hoặc cho phép giảm khối lượng đáng kể khi sử dụng nó để thay thế trong các kết cấu bằng thép các bon thông thường.In this paper, an experimental study on butt-welding technology of high strength PERFORM 700 steel plates was reported. The weldability of the base material, the adaptability of the materials to welding, and the mechanical properties of welding joints were assessed by the Radiographic testing (RT) technique, metallographic analysis, tensile test, bend test. The results show that PERFORM 700 steel has good weldability when using Kiswel K-110TK3 MAG flux-cored wire. The weld joint has fine ductility and after the bend test, there is no appearance of cracks or other defects. The welding joint reaches a high strength with yield and ultimate tensile strength of (712.0-720.0) MPa and (830.0-844.1) MPa, respectively. These results are the basis for manufacturing the high load-bearing structures and moreover, it allows a significant reduction of structural mass in comparison with conventional carbon steel structures.

1. Đọc trực tuyến

1. Đọc trực tuyến

Tạo bộ sưu tập với mã QR