ẢNH HƯỞNG CỦA NHIỆT ĐỘ TẠI VÙNG SONG PHA ĐẾN TỔ CHỨC VÀ CƠ TÍNH THÉP CB400

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: THI THANH VÂN TRAN

Ngôn ngữ: vie

Ký hiệu phân loại:

Thông tin xuất bản: Tạp chí Khoa học Công nghệ Hàng hải, 2022

Mô tả vật lý: tr.76-80

Bộ sưu tập: Báo, Tạp chí

ID: 330928

Thêm vào giỏ Liên kết toàn văn

In this work, the influence of heat treatment process in the dual phase region of CB400 steel was explored. Calculation results by thermodynamics and JmatPro software determined that temperature of phase transformation is in the range of 730-823oC for this steel. Analysis of the phase fraction showed that increasing the temperature of the dual phase heat treatment increased the martensitic fraction. With the treatment temperature at 790oC, the hardness result is 52.4HRC
strength is 960MPa and ductility is 16%. The microstructure shows that the martensite percentage is 25%
the grain of martensite is 8µm
ferrite is 12.5µm.Trong công trình này trình bày những kết quả nghiên cứu về ảnh hưởng của chế độ xử lý nhiệt ở vùng song pha của thép CB400. Các kết quả tính toán bằng nhiệt động học và phần mềm JmatPro đã xác định được nhiệt độ vùng chuyển biến song pha là từ 730 oC - 823oC cho mác thép nghiên cứu. Phân tích tỷ phần pha cho thấy tăng nhiệt độ xử lý nhiệt song pha thì tỷ phần mactenxit tăng. Với nhiệt độ xử lý ở 790oC cho được kết quả độ cứng là 52.4HRC
độ bền là 960MPa và độ dẻo là 16%. Phân tích về tổ chức cho thấy tỷ phần mactenxit là 25%
độ hạt của mactenxit là 8µm
ferit là 12,5µm.