In this paper, copper (I) oxide (Cu2O) were successfully synthesized using copper (II) sulfate (CuSO4), glucose and sodium hydroxide (NaOH). CuSO4 solution is separated from electronic waste by pyrometallurgical process combined with hydrometallurgical process. The obtained materials were studied the methods of synthesis and the influence of pH showed that slowly adding CuSO4 solution to the solution including NaOH and glucose and pH = 12 obtained Cu2O with nanostructure. Through analyzing the structural characteristics by XRD and SEM methods, it was found that the synthesized Cu2O material has a crystal size calculated by XRD method of 8.75 nm, lattice constant of 0.43 nm, the strain of 0.004
The number of dislocations presenting in the unit area of 0.013. The Cu2O particles formed are relatively uniform, the particle size is about 50 nm. Synthesized Cu2O nanomaterials both solve the problem of e-waste pollution and open up a source of raw materials for synthesizing nanomaterials.Trong bài báo này, đồng (I) oxit (Cu2O) được tổng hợp thành công từ dung dịch đồng (II) sunfat (CuSO4), glucozơ, natri hidroxit (NaOH). Dung dịch CuSO4 được tách từ rác thải điện tử theo phương pháp hỏa luyện kết hợp với thủy luyện. Vật liệu này được nghiên cứu tổng hợp bằng các phương pháp thực hiện và ảnh hưởng của pH cho thấy cho từ từ dung dịch CuSO4 vào dung dịch gồm NaOH và glucozơ có pH = 12 thu được Cu2O có cấu trúc nano. Qua việc phân tích cấu trúc bằng phương pháp XRD và SEM cho thấy tổng hợp vật liệu Cu2O có kích thước tinh thể tính theo phương pháp XRD là 8,75 nm, hằng số mạng bằng 0,43 nm, độ biến dạng bằng 0,004
mật độ lệch vị trí bằng 0,013. Các hạt Cu2O tạo thành tương đối đồng đều, kích thước hạt khoảng 50 nm. Vật liệu Cu2O có cấu trúc nano tổng hợp được vừa giải quyết vấn đề ô nhiễm rác thải điện tử, vừa tổng hợp được vật liệu nano có ứng dụng cao.