Điều chế và khan hóa muối hydrat tecbi florua theo phương pháp ướt làm nguyên liệu tinh luyện tecbi kim loại

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Bá Thuận Lê, Thanh Thủy Nguyễn, Thị Liên Nguyễn, Trọng Hùng Nguyễn

Ngôn ngữ: vie

Ký hiệu phân loại:

Thông tin xuất bản: Tạp chí Khoa học và Công nghệ Việt Nam - B, 2022

Mô tả vật lý: tr.47

Bộ sưu tập: Báo, Tạp chí

ID: 332631

Thêm vào giỏ Liên kết toàn văn

Muối hydrat tecbi florua (TbF3.nH2O) được điều chế từ dung dịch tecbi clorua (TbCl3) với các tác nhân kết tủa amoni bicacbonat (NH4HCO3) và axit hydro floric (HF). Quá trình khan hóa TbF3.nH2O được thực hiện trong lò nung ống với sự có mặt của khí argon trong quá trình nung. Ảnh hưởng của các tác nhân đến quá trình kết tủa và điều kiện khan hóa đã được nghiên cứu. Phương pháp phân tích nhiệt được áp dụng để lựa chọn khoảng nhiệt độ khan hóa. Sản phẩm thu được từ quá trình điều chế được đánh giá bằng phương pháp nhiễu xạ tia X (XRD), kính hiển vi điện tử quét (SEM) và phổ nhiễu xạ năng lượng (EDS). Kết quả cho thấy, sản phẩm TbF3 khan có độ tinh khiết cao, kích thước hạt dao động trong khoảng 200 đến 700 nm, phù hợp làm nguyên liệu để điều chế tecbi (Tb) kim loại.Terbium fluoride hydrate (TbF3.nH2O) was prepared from the terbium chloride (TbCl3) solution using ammonium bicarbonate (NH4HCO3) and hydrofluoricacid (HF) as precipitate reagents. The dehydration of TbF 3.nH2O was carried out in a tube furnace in the presence of argon. The influential factors on theproduction process have been studied. Thermal analysis techniques were applied to determine the temperature range for dehydration. The obtained TbF3 products were assessed by X-ray diffraction, Scanning electron microscopy, and Energy dispersive X-ray spectroscopy methods. The results showed that anhydrous TbF3 with a particle size of 200-700 nm can be used as a material to prepare terbium metal.

1. Đọc trực tuyến

1. Đọc trực tuyến

Tạo bộ sưu tập với mã QR