CHẾ TẠO COMPOSITE POLYANILINE/SiO2 ỨNG DỤNG TRONG LỚP SƠN PHỦ EPOXY VÀ KHẢO SÁT TÍNH CHẤT BẢO VỆ CHỐNG ĂN MÒN CHO THÉP CT3

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Văn Minh Mai, Hữu Trang Nguyễn, Tiến Nam Nguyễn, Văn Bằng Trần, Thị Đào Trịnh

Ngôn ngữ: vie

Ký hiệu phân loại:

Thông tin xuất bản: Tạp chí Khoa học và Công nghệ - Đại học Thái Nguyên, 2023

Mô tả vật lý: tr.54 - 61

Bộ sưu tập: Metadata

ID: 336997

Thêm vào giỏ Liên kết toàn văn

Bài báo trình bày về vấn đề tăng cường hiệu quả bảo vệ bề mặt thép CT3 trong môi trường khí hậu nhiệt đới bằng lớp sơn phủ có chứa polyaniline/SiO2 (PANi/SiO2). Polymer PANi/SiO2 được tổng hợp bằng phương pháp trùng hợp hóa học trong môi trường acid với nồng độ mol 1M và chất oxi hóa mạnh, sau đó pha trộn vào sơn epoxy rồi thi công lên bề mặt thép CT3 để tiến hành các thử nghiệm chống ăn mòn. Chúng tôi nhận thấy rằng khi bổ sung SiO2 vào polymer Polyaniline (PANi) rồi pha trộn với epoxy, độ bền cơ lí và khả năng chống ăn mòn cải thiện rõ rệt so với sơn có thành phần chỉ chứa lớp màng PANi đồng chất. Trong các tỉ lệ thử nghiệm, sơn với tỉ lệ thành phần PANi/SiO2 = 1/1 cho kết quả tốt nhất về độ bám dính 2,2 MPa, độ bền va đập 15 kg.cm, bề mặt màng sơn ổn định sau 3 tháng thử nghiệm tự nhiên trong điều kiện khí hậu ẩm nhiệt đới.This paper presents the problem of enhancing the protective effect of CT3 steel surface in tropical climates by coatings containing polyaniline/SiO2 (PANi/SiO2). Polymer PANi/SiO2 was synthesized by chemical polymerization in an acidic environment with a molar concentration of 1M and a strong oxidizing agent, then mixed into epoxy paint and applied to CT3 steel surface to perform anticorrosion test. We found that when SiO2 was added to polyaniline polymer (PANi) and mixed with epoxy, the mechanical strength and corrosion resistance were significantly improved compared to paints containing only PANi polymer. In the test ratios, paint with component ratio PANi/SiO2 = 1/1 gave the best results in terms of adhesion of 2.2 MPa, impact strength of 15 kg.cm, stable film surface after 3 months of natural testing in a humid tropical climate.

1. Đọc trực tuyến

1. Đọc trực tuyến

Tạo bộ sưu tập với mã QR