In this paper, the influence of nanoparticle size on magnetic properties (saturation magnetization MS, effective magnetic anisotropy Keff) and optical properties (energy band gap Eg) were investigated. Magnetic nanoparticles Fe3O4 (FO) were synthesized by co-precipitation with different reaction temperatures of 50°C, 60°C, 70°C, and 80°C. They had sizes of 8.7 nm, 10.1 nm, 10.4 nm, and 11.9 nm, respectively. While the value of saturation magnetization MS increased from 51.65 emu/g to 64.56 emu/g, their magnetic anisotropy value decreased from 18.26 kJ/m3 to 12.49 kJ/m3 when the value of diameter of magnetic nanoparticles Fe3O4 changed from 8.7 nm to 11.9 nm. In addition, the changing of the energy band gap Eg from 2.23 eV (~ 11.9 nm) to 2.75 eV (~ 8.7 nm) indicated the effect of nanoparticle size on optical properties for magnetic nanoparticles FO. The nanoparticle size is an important factor affecting the magnetic and optical properties of FO magnetic nanoparticles.Trong bài báo này, ảnh hưởng của kích thước hạt lên tính chất từ (từ độ MS, dị hướng từ hiệu dụng Keff) và tính chất quang (độ rộng vùng cấm) của các hạt nano từ Fe3O4 (FO) được khảo sát. Các hạt FO được tổng hợp bằng phương pháp đồng kết tủa với các nhiệt độ phản ứng khác nhau 50°C, 60°C, 70°C và 80°C, và kích thước tương ứng lần lượt là 8,7 nm, 10,1 nm, 10,4 nm và 11,9 nm. Trong khi từ độ MS của hạt FO tăng từ 51,65 emu/g xuống 64,56 emu/g thì giá trị dị hướng từ của chúng giảm từ 18,26 kJ/m3 đến 12,49 kJ/m3 theo chiều tăng của kích thước hạt từ 8,7 nm đến 11,9 nm. Bên cạnh đó, sự thay đổi độ rộng vùng cấm từ 2,23 eV (~ 11,9 nm) đến 2,75 eV (~ 8,7 nm) thể hiện ảnh hưởng của kích thước lên tính chất quang của mẫu FO. Kích thước hạt là yếu tố quan trọng ảnh hưởng đến tính chất từ và tính chất quang của các hạt nano từ FO.