KHẢO SÁT MỘT SỐ CHẤT HÓA DẺO CHO NHIÊN LIỆU RẮN HỖN HỢP TRÊN NỀN POLYVINYL CLORUA

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Minh Khai Đoàn, Duy Tuấn Nguyễn, Đức Nhân Phan, Quang Tuấn Trần

Ngôn ngữ: vie

Ký hiệu phân loại:

Thông tin xuất bản: Journal of Science and Technique, 2023

Mô tả vật lý: tr.5

Bộ sưu tập: Metadata

ID: 337370

Thêm vào giỏ Liên kết toàn văn

Bài báo trình bày kết quả khảo sát một số chất hóa dẻo cho nhiên liệu rắn hỗn hợp. Nhiên liệu rắn hỗn hợp được chế tạo từ PVC hóa dẻo bởi DOP, DOA và hỗn hợp DOP/DOA với chất oxi hóa ammoni peclorat (AP), chất cháy bột nhôm (Al) và xúc tác cháy bột sắt (III) oxit (Fe2O3). Các tính chất cơ học và đặc trưng nhiệt đã được xác định. Kết quả cho thấy các mẫu nhiên liệu có các đặc trưng đáp ứng được yêu cầu của nhiên liệu rắn hỗn hợp như: mô đun đàn hồi 176,7 ÷ 202,9 MPa, độ biến dạng 28 ÷ 45 %, nhiệt độ bùng cháy 304,8 ÷ 308,4°C và độ bền nhiệt 0,081 ÷ 0,178 ml/g. Chất hóa dẻo DOP có hiệu quả hóa dẻo PVC tốt hơn so với DOA. Bên cạnh đó, nhiên liệu được hóa dẻo bởi DOA gây ra giảm khối lượng mạnh hơn khi già hóa và độ bền nhiệt thấp hơn so với DOP.This article presents an investigation of some plasticizers for composite solid propellants. The samples are prepared from the PVC plasticized by the DOP, DOA, and a mixture of DOP/DOA with ammonium perchlorate (AP) oxidizer, aluminum (Al) powder, and iron (III) oxide (Fe2O3). Mechanical properties and thermal characteristics of the samples were determined. The results show that the characteristics of the samples meet the requirements of composite solid propellant such as elastic modulus 176.7 ÷ 202.9 MPa, deformation 28 ÷ 45 %, ignition temperature 304.8 ÷ 308.4°C and thermal stability 0.081 ÷ 0.178 ml/g. The DOP plasticizer is a better effect on plasticization than the DOA. In addition, the sample from PVC/DOA causes more loss of weight and lower thermal stability than that from PVC/DOP.

1. Đọc trực tuyến

1. Đọc trực tuyến

Tạo bộ sưu tập với mã QR