NGHIÊN CỨU ẢNH HƯỞNG CỦA PHỤ GIA NANOSILICA TỚI TÍNH CHẤT CƠ HỌC VÀ NHIỆT CỦA NHỰA PA610

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Thị Hương Thủy Hoàng, Hoàng Thanh Lê, Thị Thúy Hằng Lê, Như Hải Lương, Thế Hữu Nguyễn, Thế Long Phạm

Ngôn ngữ: vie

Ký hiệu phân loại:

Thông tin xuất bản: Tạp chí Khoa học & Công nghệ - Trường Đại học Công nghiệp Hà Nội, 2022

Mô tả vật lý: tr.124

Bộ sưu tập: Metadata

ID: 337741

Thêm vào giỏ Liên kết toàn văn

In this paper, the influence of nanosilica on the mechanical and thermalproperties of PA610 plastic was investigated. The optimal content of nanosilicawas determined through the mechanical properties and morphological ofPA610/nanosilica nanocomposite. The results show that the maximum tensilestrength of nanocomposites with nanosilica content is 3%. At this content, thethermal stability of PA610/nanosilica nanocomposite is significantly improvedcompared to neat PA610, as shown by an increase in the decomposition onsettemperature of 23.43oC.Trong bài báo này, ảnh hưởng của nanosilica đến các tính chất cơ học vànhiệt của nhựa PA610 đã được nghiên cứu. Hàm lượng tối ưu của nanosilica đượcxác định thông qua các tính chất cơ học và cấu trúc hình thái của vật liệuPA610/nanosilica nanocomposite. Kết quả cho thấy, độ bền kéo đứt của vật liệunanocomposite đạt giá trị lớn nhất với hàm lượng nanosilica là 3%. Ở hàm lượngnày, độ ổn định nhiệt của vật liệu PA610/nanosilica nanocomposite được cảithiện đáng kể so với nhựa PA610 ban đầu, thể hiện qua sự gia tăng nhiệt độ bắtđầu phân hủy là 23,43oC.