NiS as an electrode material for electrochemical capacitors has been synthesized by chemical and hydrothermal methods. The results show that the synthesized NiS is in amorphous form, increasing the reaction temperature or hydrothermal time tends to reduce the porosity of the materials. NiS synthesized by hydrothermal method exhibits better electrochemical properties than those synthesized by chemical method. NiS synthesized at the optimal condition of a hydrothermal temperature of 140 oC in 5h has a specific capacitance of 1592 F\g (265 mAh\g) and 1567 F\g (261 mAh\g) at a scan rate of 5 mV\s and a current density of 5 A\g, respectively. This value is about 88% of the theoretical value of NiS and is maintained after 25 continuous charge-discharge cycles at different current densities ranging from 5 to 40 A\g.NiS theo định hướng làm vật liệu điện cực cho tụ điện hóa đã được tổng hợp bằng phương pháp hóa học và phương pháp thủy nhiệt. Kết quả cho thấy NiS tổng hợp được ở dạng vô định hình, tăng nhiệt độ phản ứng hoặc tăng thời gian thủy nhiệt có xu hướng làm giảm độ xốp của vật liệu. Vật liệu NiS tổng hợp bằng phương pháp thủy nhiệt thể hiện tính chất điện hóa tốt hơn vật liệu tổng hợp bằng phương pháp hóa học. NiS thu được bằng cách thủy nhiệt ở 140 oC trong 5 giờ có điện dung riêng tại tốc độ quét thế 5 mV\s và tại mật độ dòng 5A\g lần lượt là 1592 F\g (265 mAh\g) và 1567 F\g (261 mAh\g). Giá trị này bằng khoảng 88% giá trị lí thuyết của NiS và được duy trì sau các chế độ nạp-phóng liên tục mỗi 25 chu kì liên tiếp ở các mật độ dòng khác nhau nằm trong khoảng 5 40A\g.