NGHIÊN CỨU CÔNG NGHỆ ĐÚC VÀ XỬ LÝ NHIỆT NHẰM NÂNG CAO KHẢ NĂNG LÀM VIỆC CHO BÚA NGHIỀN TỪ THÉP MANGAN CAO

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: THỊ THANH VÂN TRẦN

Ngôn ngữ: vie

Ký hiệu phân loại:

Thông tin xuất bản: Tạp chí Khoa học Công nghệ Hàng hải, 2023

Mô tả vật lý: tr.51

Bộ sưu tập: Metadata

ID: 341569

Thêm vào giỏ Liên kết toàn văn

High manganese austenitic steel is widely used as parts to withstand impact and abrasion loads in the quarrying, ore industries, etc. The research to improve quality and reduce costs thanks to the application of advanced casting technologies is becoming increasingly important. development direction of this steel line. The improvement of steel quality has been proven by world scientists, but steel casting technology is not easy and needs researching. The article introduces some research results of casting technology in glass-sand-water mold for steel hammer details. The results show that the given casting technology and heat treatment regime have improved the quality of Mn13 steel and ensured the mechanical properties of the details.The mechanical property value obtained after applying the heat treatment regime is the impact toughness reaching 121J/cm2
hardness value is 260HB
The strength limit is 586Mpa and the elongation is 24.5%, which is in the working condition well.Thép austenit mangan cao được dùng rộng rãi làm các chi tiết chịu tải mài mòn va đập trong công nghiệp khai thác đá, quặng,… Việc nghiên cứu nâng cao chất lượng, hạ giá thành nhờ ứng dụng các công nghệ đúc tiên tiến đang là hướng phát triển của dòng thép này. Việc cải thiện chất lượng thép đã được các nhà khoa học thế giới chứng minh, nhưng công nghệ đúc thép thì không dễ dàng và cần nghiên cứu. Bài báo giới thiệu một số kết quả nghiên cứu công nghệ đúc trong khuôn cát-nước thủy tinh cho chi tiết búa nghiền làm bằng thép. Kết quả cho thấy công nghệ đúc và chế độ xử lý nhiệt đưa ra đã cải thiện chất lượng thép Mn13 và đảm bảo được cơ tính cho chi tiết. Giá trị cơ tính đạt được sau khi áp dụng theo chế độ xử lý nhiệt là độ dai va đập đạt 121 J/cm2
giá trị độ cứng đạt được là 260HB
giới hạn bền 586Mpa và độ giãn dài là 24.5 %, đáp ứng tốt điều kiện làm việc.