The polypropylene/silica sand powder polymer composite materials were fabricated by using the melt mixing method in a Haake internal mixer at 190oC. The influence of size and BCSi content on melt rheology, mechanical properties, and structural morphology was investigated. The results show the torque of the PP/BCSi composite material decreased as the BCSi content increased from 10 to 30% wt, but then increased at 40% and 50% wt. The tensile strength, elongation, and impact strength of the PP/BCSi composite were lower than that of PP, but the hardness was higher. When comparing PP/BCSi composites made with silica sand powder modified with steric acid (BCSiA) to unmodified (BCSi), those made with BCSiA had higher mechanical properties. By studying SEM images of the composite surface, we observed that BCSiA increased phase interaction, adhesion, and dispersibility of BCSi into the PP plastic substrate.Vật liệu compozit PP/BCSi được chế tạo bằng phương pháp trộn nóng chảy ở190oC trên máy Haake Rheomixer. Đã khảo sát ảnh hưởng của kích thước, hàm lượng BCSi đến lưu biến nóng chảy, tính chất cơ học và hình thái cấu trúc. Kết quảthu được cho thấy ban đầu khi hàm lượng BCSi tăng từ 10 đến 30% khối lượng, mô men xoắn của vật liệu compozit PP/BCSi giảm sau đó lại tăng khi hàm lượng BCSi trong mẫu chiếm 40%, 50% khối lượng. Độ bền kéo đứt, độ dãn dài khi đưt, độ bền va đạp của compozit PP/BCSi thấp hơn so với PP nhưng độ cứng cao hơn. So sánh tính chất cơ học của vật liệu compozit PP/BCSi sử dụng bột cát silica biến tính bằng axit steric (BCSiA) cao hơn so với chưa biến tính (BCSi). Nghiên cứu ảnh SEM bẻ gãy bề mặt vật liệu compozit cho thấy, BCSiA làm tăng tương tác pha, độbám dính và khả năng phân tán của BCSi vào trong nền nhựa PP.