In this article, the results were presented on changing of microstructure of CuAl9Fe4Ni2 alloy after casting
quenching and tempering. The microstructure were found to be martensitic phases
residual α phase and the intermetallic phase of Fe and Al. By OM, the article has shown that the heat treatment process for alloy hardness is uniform annealing at 850oC for 02 hours and cooling in water, then tempering at 350oC for 02 hours which was the highest hardness value.Trong công trình này trình bày các kết quả nghiên cứu về sự biến đổi tổ chức tế vi của hợp kim CuAl9Fe4Ni2 sau các trạng thái đúc
tôi và ram. Tổ chức tế vi được tìm thấy là các pha mactenxit
pha α còn dư và pha liên kim của Fe và Al. Bằng tối ưu hóa, công trình đã chỉ ra quy trình xử lý nhiệt tối ưu về độ cứng của hợp kim là ủ đồng đều hóa và tôi ở 850oC trong 02 giờ sau đó ram ở 350oC trong 02 giờ cho giá trị độ cứng cao nhất.