Ảnh hưởng của thời gian bảo dưỡng đến cường độ nén của bê tông tự lèn có hàm lượng tro bay cao

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: TRUNG DUC BUI, DANG NHAT MINH NGUYEN, PHD NGUYEN HUNG CUONG, PHD TRAN QUANG DUNG

Ngôn ngữ: vie

Ký hiệu phân loại:

Thông tin xuất bản: Tạp chí Xây dựng, 2024

Mô tả vật lý: tr.136

Bộ sưu tập: Metadata

ID: 381177

Thêm vào giỏ Liên kết toàn văn

Bài báo trình bày kết quả nghiên cứu thực nghiệm về sự ảnh hưởng của thời gian bảo dưỡng đến cường độ nén của bê tông tự lèn (BTTL) có hàm lượng tro bay cao. Các cấp phối BTTL trong nghiên cứu có tỷ lệ tro bay lần lượt 0%, 50% và 60% thể tích bột. Các mẫu bê tông được tiến hành bảo dưỡng bằng ngâm nước với thời gian 28 ngày và 90 ngày. Kết quả thí nghiệm cho thấy kéo dài thời gian bảo dưỡng có tác dụng tăng cường độ nén ở độ tuổi muộn của BTTL có hàm lượng tro bay cao. Khi thời gian bảo dưỡng ngâm nước tăng từ 28 ngày lên 90 ngày, các cấp phối có hàm lượng tro bay 50% và 60% có giá trị cường độ nén ở tuổi 90 ngày tăng lần lượt 3.7% và 8.7%. Tuy nhiên, đối với mẫu BTTL không sử dụng tro bay, việc tăng thời gian bảo dưỡng từ 28 ngày lên 90 ngày, giá trị cường độ nén tăng không đáng kể, chỉ khoảng 0.99%. Từ khóa: Bê tông tự lèn
tính công tác
cường độ nén bê tôngThis paper presents the experimental findings on the influence of curing duration on the compressive strength of self-compacting concrete (SCC) with a high proportion of fly ash. The SCC mixtures examined had fly ash content ratios of 0%, 50%, and 60% by volume of powder. The concrete samples were subjected to water immersion curing for periods of 28 and 90 days. The experimental data revealed that prolonging the curing duration positively impacted the compressive strength of SCC with high fly ash content at later stages. Specifically, when the water immersion curing period was extended from 28 to 90 days, the compressive strength values at 90 days of the mixtures with 50% and 60% fly ash content increased 3.7% and 8.7%, respectively. Conversely, for the samples without fly ash, extending the curing period from 28 to 90 days resulted in a negligible increase in terms of compressive strength, approximately 0.99%. Keywords: Self-compacting concrete
fly ash
curing time
workability
compressive strength of concrete.