Chế tạo Cu2O dạng cubic và khảo sát hoạt tính xúc tác quang của vật liệu

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Xuân Dự Đặng, Thị Giang Anh Phạm

Ngôn ngữ: Vie

Ký hiệu phân loại: 620 Engineering and allied operations

Thông tin xuất bản: Tạp chí Công Thương 2023

Mô tả vật lý: 324-329

Bộ sưu tập: Metadata

ID: 399181

Thêm vào giỏ Liên kết toàn văn

Trong nghiên cứu này, đồng (I) oxit (Cu2O) dạng cubic đã được chế tạo sử dụng axit ascorbic và glucose làm chất khử. Vật liệu được đặc trưng bằng giản đồ nhiễu xạ tia X (XRD) và phổ FT-IR. Hình thái và kích thước hạt được phân tích bằng phương pháp SEM và TEM. Kết quả cho thây chất khử có ảnh hưởng đến hình thái cũng như kích thước hạt. Cu2O chế tạo được có độ tinh khiết cao. Với chất khử axit ascorbic, các hạt Cu2O hình thành có dạng cubic đồng đều, kích thước hạt khoảng 75 nm. Khi sử dụng chất khử glucose, Cu2O có dạng cubic không đồng đều, nhấn bóng, kích thước hạt khoảng 1,37 micromet. Cu2O cubic có khả năng hấp phụ tháp đối với RhB, hiệu suất xử lý RhB tối đa đạt được là 25%. Hoạt tính xúc tác quang của Cu2O cubic không đồng đều tốt hơn so với cubic đồng đều. Hiệu suất xử lý RhB của Cu2O dạng cubic không đồng đều đạt được là 43% sau 210 phút xử lý., Tóm tắt tiếng anh, In this study, cubic cuprous oxide (Cu2O) is successfully fabricated by using ascorbic acid and glucose as reducing agents. The formation of cubic cuprous oxide is confirmed through XRD and FT-IR methods. The morphology and particle size of the material are characterized by SEM and TEM. The results show that reducing agents are effective in the morphology and particle size of the material. The fabricated cubic cuprous oxide particles exhibit a high purity. In case of ascorbic acid as a reducing agent, the formed Cu2O particles are in a uniform cubic shape with a particle size of about 75 nm. When glucose is used as a reducing agent, the obtained Cu2O has a non uniform and smooth cubic shape with a particle size of about 1.37 micrometers. The obtained cubic Cu2O exhibit a low adsorption capacity for RhB. The maximum RhB treatment efficiency is 25%. The photocatalytic activity of the non uniform cubic Cu2O is better than that of the uniform cubic Cu2O. The RhB treatment efficiency of non uniform cubic Cu2O achieves 43% after 210 minutes.

1. Đọc trực tuyến

1. Đọc trực tuyến

Tạo bộ sưu tập với mã QR