Ảnh hưởng của nồng độ nb đến một số tính chất quang, điện của hệ gốm BNKT

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Thị Ánh Nhạn Lê, Đình Giớ Phan

Ngôn ngữ: Vie

Ký hiệu phân loại: 620.1 Engineering mechanics and materials

Thông tin xuất bản: Tạp chí Khoa học và công nghệ Trường Đại học Khoa học, Đại học Huế, 2020

Mô tả vật lý: 17-30

Bộ sưu tập: Metadata

ID: 417504

Thêm vào giỏ Liên kết toàn văn

Hệ gốm sắt điện không chì Bi0,5(Na0,82K0,18)0.5(Ti1-xNbx)O3 (viết tắt là BNKT-xNb), với x = 0, 0,01, 0,015, 0,02, 0,03, 0,04, đã được chế tạo bằng công nghệ gốm truyền thống. Ảnh hưởng của nồng độ Nb đến vi cấu trúc và một số tính chất quang, điện của hệ gốm đã được nghiên cứu chi tiết. Kết quả thực nghiệm cho thấy khi gia tăng nồng độ Nb, mật độ gốm gia tăng và đạt giá trị cao nhất (5,92 g/cm3) tại nồng độ x = 0,02 mol, bên cạnh đó, kích thước hạt giảm, vi cấu trúc đồng đều, các hạt xếp chặt. Tương ứng vi cấu trúc dày đặc với các hạt nhỏ mịn, độ truyền qua quang học của mẫu gốm có nồng độ x = 0,02 mol đạt giá trị cao nhất trên 41% ứng với bước sóng 790 nm và 36% ứng với bước sóng 680nm và có độ rộng vùng năng lượng cấm lớn nhất (Eg = 2,78 eV). Nhiệt độ khử phân cực Td và nhiệt độ Curie TC tăng tương ứng từ 65oC đến 145oC và từ 187oC đến 234oC khi nồng độ Nb gia tăng. Gốm thể hiện đặc trưng của một sắt điện relaxor., Tóm tắt tiếng anh, Bi0.5(Na0.82K0.18)0.5(Ti1-xNbx)O3 ceramic system (abbreviated BNKT_ xNb) with x = 0.0, 0.01, 0.015, 0.02, 0.03, 0.04, has been fabricated by the conventional solid-state reaction method. The effects of Nb content on the microstructure and some optical and electrical properties were studied in detail. The experimental results showed that with increasing Nb concentration, the ceramic density increased and reached the highest value (5.92 g/cm3) at x = 0.02mol, besides, the grain size of the ceramics decreased, the microstructure more uniform, the particles are packed with clear grain boundaries, less pores. With the dense microstructure and fine small particles, the optical transmission of the ceramics is strong, the ceramic sample with x = 0.02 mol exhibits stably high transmittance above 41% for the wavelength of 790nm and 36% at the wavelength of 680nm and has the largest optical band gap energy (Eg = 2.78 eV).The depolarization temperature (Td) and Curie temperature (TC ) increase from 65oC to 145oC and 187oC to 234oC, respectively, when the concentration of Nb increases. The broadness of dielectric peak around Tm indicated a diffusive phase transition for all compositions suggesting the relaxor-like behavior of BNKT_ xNb ceramic systems.

1. Đọc trực tuyến

1. Đọc trực tuyến

Tạo bộ sưu tập với mã QR