Ảnh hưởng của sợi thép đến đặc tính kỹ thuật của bê tông cường độ cao

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Nhât Long Phan, Khánh Dung Trần, Duy Hải Võ

Ngôn ngữ: Vie

Ký hiệu phân loại: 691 Building materials

Thông tin xuất bản: Tạp chí Khoa học và Công nghệ Đại học Đà Nẵng, 2020

Mô tả vật lý: 16-19

Bộ sưu tập: Metadata

ID: 419440

Thêm vào giỏ Liên kết toàn văn

Nghiên cứu này khảo sát sự ảnh hưởng của sợi thép đối với tính chất của bê tông cường độ cao. Các cấp phối được thiết kế dựa trên phương pháp DMDA. Theo phương pháp này, tro bay đóng vai trò vừa làm đặc chắc các lỗ rỗng giữa các hạt cốt liệu, vừa tham gia phản ứng pozzolanic. Tỉ lệ nước trên chất kết dính ở tất cả cấp phối đều là 0.27 nhằm tạo ra bê tông cường độ cao. Trong khi đó, phụ gia siêu dẻo được bổ sung để đảm bảo độ sụt của bê tông tươi. Các thí nghiệm độ sụt, cường độ nén, vận tốc xung siêu âm, và điện trở suất bề mặt cho thấy các tính chất rất khả quan của bê tông cường độ cao bổ sung sợi thép. Cấp phối với 5% sợi thép cho cường độ nén lớn nhất với 74.9 MPa. Thông qua các thí nghiệm, tăng hàm lượng sợi thép gia tăng cường độ nén và vận tốc xung siêu âm nhưng làm giảm độ sụt và điện trở suất bề mặt của bê tông cường độ cao., Tóm tắt tiếng anh, This research investigated significant effects of steel fiber on engineering properties of high-strength concrete. The mix proportions were designed relied on the Densified Mixture Design Algorithm (DMDA) method in which fly ash (FA) had filler and pozzolanic effects. The water-to-binder ratio (w/b) was kept at 0.27 to achieve high strength while the superplasticizer was added to ensure the workability of high-strength concrete. Slump, compressive strength, ultrasonic pulse velocity (UPV) and electrical surface resistivity (ESR) tests were examined. All of the steel fiber concrete specimens performed exceptional engineering properties. The greatest compressive strength obtained in this study was 74.9 MPa when steel fiber accounted for 5% by weight of fine aggregate. The amount of steel fiber was proportional to strength, UPV but inversely related with workability and ESR of the high-strength concrete.

1. Đọc trực tuyến

1. Đọc trực tuyến

Tạo bộ sưu tập với mã QR