NGHIÊN CỨU CHẾ TẠO VẬT LIỆU MnO2/GRAPHENE COMPOSITE VÀ KHẢ NĂNG ỨNG DỤNG LÀM VẬT LIỆU ĐIỆN CỰC DƯƠNG CHO PIN KIM LOẠI Zn

• Tác giả: Tiến Phát Đoàn, Ngọc Khánh Nguyễn, Bảo Châu Tạ, Thị Hương Giang Trần, Thị Kim Chi Trần
• Ngôn ngữ: vie
• Thông tin xuất bản: Tạp chí Phân tích Hóa, Lý và Sinh học, 2024
• Mô tả vật lý: tr.146
• Bộ sưu tập: Metadata
• ID: 462181

Tóm tắt

This report presents the synthesis of MnO2 by the chemical precipitation method and graphene oxide by improved Hummers’ method. Graphene was produced by reducing graphene oxide. TEM observation and X-ray diffraction confirmed that the synthesized MnO2 has a nanorod form with an α-MnO2 structure. Graphene oxide formation was verified through Raman scattering spectroscopy with two characteristic peaks at 1344 cm-1and 1591 cm-1. When combining MnO2 with graphene to form a cathode for zinc-ion batteries, the results indicated the potential of this composite as a cathode, showing an initial specific capacity of 40 mAh/g after 3 cycles.