This study explored the use of glutaraldehyde-crosslinked polyvinyl alcohol (PVA) membranes for the pervaporation separation of an 80 wt% ethanol/water mixture at 60°C. The effects of heat treatment on the pervaporation performance of the crosslinked PVA membranes were systematically examined. Physicochemical properties of the membranes were characterized using thermogravimetric analysis (TGA), X-ray diffraction (XRD), water contact angle measurements, and swelling tests. Results show that heat treatment is essential to complete the crosslinking reaction, significantly improving membrane selectivity. Additionally, heat treatment at 60°C proved optimal for enhancing the pervaporation performance of glutaraldehyde-crosslinked PVA membranes in ethanol/water separation applications.Trong nghiên cứu này, các màng PVA được nối mạng bằng glutaraldehyde để tách hỗn hợp ethanol/nước với nồng độ 80 %kl bằng phương pháp thẩm thấu-bốc hơi ở nhiệt độ 60°C. Ảnh hưởng của nhiệt độ xử lý nhiệt lên hiệu quả thẩm thấu-bốc hơi của màng PVA nội mạng đã được khảo sát. Phân tích nhiệt trọng lượng (TGA), XRD, đo góc tiếp xúc với nước, và thử nghiệm độ trương nở được thực hiện để đánh giá các tính chất lý hóa của màng thu được. Kết quả cho thấy xử lý nhiệt là yếu tố quan trọng để hoàn thiện phản ứng nối mạng, từ đó tăng khả năng chọn lọc của màng PVA được nối mạng. Hơn nữa, xử lý nhiệt màng PVA được nối mạng bằng glutaraldehyde ở 60°C là thích hợp cho quá trình phân tách hỗn hợp ethanol/nước bằng phương pháp thẩm thấu-bốc hơi.