Eu3+ and Bi3+ co-doped Gd3PO7 host lattice with different Bi3+ concentrations have been synthesized via solid state reaction. The structural characteristic and morphology of sample surface were investigated by X-ray diffraction and SEM image techniques. Influence of the existence of Bi3+ ions on emission intensity of luminescence Eu3+ ions in Gd3PO7 host lattice was studied by the photoluminescence spectra and Judd-Ofelt theory. In which, informatin of R ratio and Ω2 intensity parameter from the Judd-Ofelt theory reveals the increase in the assymmetry at Eu3+ sites in Gd3PO7 host lattices in the sample containg Bi3+ ions. The CIE chromaticity coordinates and correlated color temperature (CCT) were also used to characterize the overall emitted emission of Gd3PO7:Eu3+,Bi3+ phosphors with various Bi3+ concentrations.Eu3+ và Bi3+ đồng pha tạp vật liệu Gd3PO7 với các nồng độ Bi3+ khác nhau đã được tổng hợp bằng phương pháp pha rắn. Đặc trưng cấu trúc và hình thái bề mặt vật liệu được khảo sát bằng kỹ thuật phân tích nhiễu xạ tia X và ảnh hiển vi điện tử quét SEM. Ảnh hưởng của sự tồn tại ion Bi3+ đến sự phát quang phát xạ của ion Eu3+ trong mạng nền Gd3PO7 được nghiên cứu bằng phổ phát quang và lý thuyết Judd-Ofelt. Trong đó, thông tin về tỉ số cường độ R và tham số cường độ Ω2 thu từ lý thuyết Judd-Ofelt cho thấy sự gia tăng tính bất đối xứng tại các vị trí Eu3+ trong mạng nền Gd3PO7 của các mẫu chứa Bi3+. Tọa độ màu CIE và nhiệt độ màu (CCT) cũng được sử dụng để đánh giá phát xạ tổng thể của vật liệu phát quang Gd3PO7:Eu3+,Bi3+ với các nồng độ Bi3+ khác nhau.