Nghiên cứu phân tán siêu âm của silica có cấu trúc nano cho ứng dụng vật liệu nanocomposite=Investigating ultrasonic dispersion of nanostructured silica for nanocomposite materials application

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Thi Thuy Hang Phan

Ngôn ngữ: vie

Ký hiệu phân loại:

Thông tin xuất bản: Tạp chí Khoa học và Công nghệ - Đại học Đà Nẵng, 2024

Mô tả vật lý: tr.52-56

Bộ sưu tập: Metadata

ID: 477827

Thêm vào giỏ

Bài báo này trình bày kết quả nghiên cứu ảnh hưởng của sự phân tán siêu âm của silica có cấu trúc nano đã được chuyển từ nanosilica (n-SiO2) vào nhựa polyester không bão hòa (UPE) để ứng dụng vật liệu nanocomposite. Phương pháp kính hiển vi điện tử quét (SEM) đã được sử dụng để phân tích các đặc tính phân tán trong công trình này. Các yếu tố siêu âm phù hợp tối ưu đã được xác định bao gồm biên độ tần số siêu âm 60%, thời gian siêu âm 120 phút. Ngoài ra, kết quả đo độ bền uốn của các mẫu nanocomposite đã chỉ ra rằng việc bổ sung vật liệu nanosilica đã làm tăng đáng kể các tính chất cơ học của vật liệu nanocomposite trên cơ sở nhựa UPE. Điều này cũng cho thấy khả năng sử dụng n-SiO2 làm tác nhân gia cường cho các ứng dụng vật liệu nanocomposite.This article presented the results of investigating the influence of ultrasonic dispersion of nanostructured silica that has been referred to nanosilica (n-SiO2) into unsaturated polyester (UPE) resin for nanocomposite materials application. Scanning electron microscopy (SEM) method was employed to analyze the dispersion characteristics in this work. The optimally suitable ultrasonic factors have been identified including ultrasound frequency amplitude of 60%, ultrasound time of 120 minutes. Also, the bending strength measurement results of nanocomposite samples have shown that nanosilica material addition has increased significantly the mechanical properties of the nanocomposite material based on UPE resin. This also has shown the possibility of using n-SiO2 as a reinforcing agent for nanocomposite materials applications.

1. Đọc trực tuyến

1. Đọc trực tuyến

Tạo bộ sưu tập với mã QR