ẢNH HƯỞNG CỦA CHẾ ĐỘ HÓA GIÀ ĐẾN TỔ CHỨC TẾ VI VÀ CƠ TÍNH MỐI HÀN Ti6Al4V VỚI Ti-CP=INFLUENCE OF AGING PROCESS ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF Ti6Al4V

ẢNH HƯỞNG CỦA CHẾ ĐỘ HÓA GIÀ ĐẾN TỔ CHỨC TẾ VI VÀ CƠ TÍNH MỐI HÀN Ti6Al4V VỚI Ti-CP=INFLUENCE OF AGING PROCESS ON THE MICROSTRUCTURE AND MECHANICAL PROPERTIES OF Ti6Al4V - Ti-CP WELDING ZONE

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Anh Xuân Nguyễn, Mai Khánh Phạm, Mạnh Thắng Sái

Ngôn ngữ: vie

Ký hiệu phân loại:

Thông tin xuất bản: Tạp chí Khoa học Công nghệ Hàng hải, 2024

Mô tả vật lý: tr.61

Bộ sưu tập: Báo, Tạp chí

ID: 479738

Thêm vào giỏ

Hàn TIG hợp kim Ti6Al4V và Ti-CP (ASTM Grade 2), tiến hành thử kéo mối hàn ở các trạng thái khác nhau gồm mối hàn không được xử lý nhiệt, được xử lý nhiệt gồm tôi và hóa già ở một số chế độ khác nhau, khảo sát sự thay đổi độ cứng và tổ chức tế vi mối hàn. Kết quả tổ chức cho thấy sự phân bố nguyên tố mối hàn ở vùng chuyển tiếp khuếch tán hợp kim có độ lớn khoảng (7÷8)µm, đặc điểm vùng này hầu như không thay đổi kích thước khi xử lý nhiệt. Kết quả cho thấy xử lý nhiệt ảnh hưởng không đáng kể tới độ bền mối hàn nhưng ảnh hưởng tới độ giãn dài của hợp kim, sự phá hủy mối hàn chủ yếu xảy ra tại vùng lân cận mối hàn vùng ảnh hưởng nhiệt (HAZ) về phía Ti-CP. Mẫu hàn Ti-CP và Ti6Al4V khi xử lý nhiệt gồm tôi 900oC-2h, hóa già 525oC cho giãn dài cao hơn so với trạng thái ủ và hóa già ở nhiệt độ 400oC và 650oC.TIG welding of two different titanium alloys Ti6Al4V and Ti-CP (ASTM Grade 2) with Ti6Al4V, conducting tensile test of welds in different states: after welding, heat treatment includes quenching and aging in several different modes, investigating the change about hardness and microstructure of the weldding zone. The microstructure results show that the weld element distribution in the alloy diffusion transition zone has a distance of (7÷8)µm, the characteristics of this zone almost do not change in size when heat treated. The results show that heat treatment has a negligible effect on weld strength but affects the elongation of alloy. The weld destruction mainly occurs in the vicinity of the weld in the heat-affected zone (HAZ) towards Ti-CP. Weldding samples of Ti-CP and Ti6Al4V when heat treated include quenching at 900oC-2h, and curing at 525oC for higher elongation compared to annealing and aging at temperatures of 400oC and 650oC.