The ceramic compositions of Bi0.86Dy0.14Fe1-xTixO3 (x = 0.02-0.1) were synthesized by solid-state reaction method to study the structural phase formation and the characteristic of weak ferromagnetism. X-ray diffractions and Rietveld analysis revealed the mixed structural phase of the R3c rhombohedral and Pnma orthorhombic structures in the entire composition range. The Pnma phase percentage was found to increase significantly at a higher dopant concentration. This tendency was further confirmed by Raman spectroscopic studies, where the phonon modes of the R3c symmetry were extinguished by an increase in Ti concentration. Scanning electron micrographs revealed two distinct grain sizes reflecting the coexistence of biphasic composition. The weak ferromagnetism was emerged, however, the Ti doping resulted in degraded magnetic properties despite the fact that Ti-substitution made a complete destruction of the cycloidal spin structure in the Pnma phase.Vật liệu gốm Bi0.86Dy0.14Fe1-xTixO3 (x = 0,02-0,1) được tổng hợp bằng phương pháp phản ứng ở trạng thái rắn để nghiên cứu sự hình thành pha cấu trúc và tính chất sắt từ yếu. Giản đồ nhiễu xạ tia X (XRD) và phân tích Rietveld cho thấy sự đồng tồn tại của hai pha cấu trúc hình thoi R3c và trực giao Pnma trong tất cả các mẫu với nồng độ pha tạp Ti tăng từ x = 0,02 đến x = 0,1. Phần trăm thể tích của pha Pnma tăng đáng kể khi nồng độ pha tạp Ti tăng cao. Điều này còn được xác nhận thêm bởi các nghiên cứu quang phổ Raman, trong đó các mode dao động phonon đặc trưng cho nhóm đối xứng R3c bị triệt tiêu do sự gia tăng nồng độ Ti. Ảnh hiển vi điện tử quét (SEM) cho thấy hai vùng kích thước hạt riêng biệt phản ánh sự đồng tồn tại của hai thành phần pha. Tính chất sắt từ yếu được hình thành tại vùng biên pha cấu trúc, tuy nhiên, sự pha tạp Ti đã dẫn đến tính chất từ bị suy giảm mặc dù thực tế là sự thay thế Ti đã phá hủy hoàn toàn cấu trúc spin xoắn ở pha cấu trúc Pnma.