Ảnh hưởng của ăn mòn cưỡng bức đến ứng xử kéo của cốt thép bị ăn mòn=Influence of artificial accelerated cyclic corrosion on tensile behavior of reinforcement in concrete

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Dinh Thien Vuong Doan, Thanh Hung Nguyen, Phd Duy Kien Dao

Ngôn ngữ: vie

Ký hiệu phân loại:

Thông tin xuất bản: Tạp chí Xây dựng, 2024

Mô tả vật lý: tr.190

Bộ sưu tập: Báo, Tạp chí

ID: 484238

Thêm vào giỏ

Nghiên cứu này tập trung vào việc phân tích ứng xử kéo của cốt thép trong các kết cấu bê tông cốt thép chịu ăn mòn cưỡng bức. Mẫu thí nghiệm được tạo ra nhằm phản ánh chính xác điều kiện làm việc thực tế của kết cấu bê tông cốt thép chịu ăn mòn. Ba loại mẫu thí nghiệm tương ứng với ba loại đường kính cốt thép là 12mm, 16mm, 20mm, mác bê tông B25, B35 và B45, được ngâm trong bể chứa dung dịch NaCl 3,5% trong các khoảng thời gian nhất định. Các mẫu thép sau khi thử ăn mòn được đưa vào phân thích bằng thí nghiệm kéo. Kết quả cho thấy, tải trọng - chuyển vị cực đại giảm từ D20, D16 và D12. Không có sự khác biệt giữa các mẫu nhưng ở mẫu D16 và D20, chúng ta có thể thấy rõ điều này. Dựa trên điều này, đường kính cốt thép càng nhỏ thì sự kết nối giữa cốt thép và bê tông càng hiệu quả. Khả năng chịu lực giảm tới 40%, biến dạng giảm tới 35%. Từ khóa: Ăn mòn cục bộ
thí nghiệm ăn mòn cưỡng bức
ứng xử kéo
định luật Faraday.This study focuses on analyzing the tensile behavior of accelerated corrosion of rebar in reinforced concrete structures. The test specimens were created to accurately reflect the actual working conditions of reinforced concrete structures subjected to corrosion. Three types of test specimens corresponding to three types of rebar diameters of 12mm, 16mm, 20mm, concrete grades B25, B35 and B45, were immersed in a tank of 3.5% NaCl solution for certain periods of time. The steel specimens after the corrosion test were put into the tensile test. The results indicated that, the maximum load - slipping displacement reduce from D20, D16 and D12. There are no difference between specimens but in D16 and D20 ones, we can see this thing clearly. Based on this, the smaller diameter of rebar the more effectively connect between rebar and concrete. The bearing capacity decreased up to 40%, the deformation decreased up to 35%. Keywords: Local corrosion
accelerated cyclic corrosion test
tensile behavior
Faraday principle.