Tổng hợp và phân tích đường cong tích phân nhiệt phát quang của LiAlO2=Synthesis and analysis of thermoluminescence glow curve of LiAlO2

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Đức Kỳ Bùi, Thị Thu Hà Nguyễn, Văn Giáp Trịnh

Ngôn ngữ: vie

Ký hiệu phân loại:

Thông tin xuất bản: Tạp chí Khoa học và Công nghệ Việt Nam - B, 2025

Mô tả vật lý: tr.1

Bộ sưu tập: Metadata

ID: 486367

Thêm vào giỏ

Chế tạo vật liệu LiAlO2 bằng phương pháp sol-gel kết hợp với một loại axit hữu cơ (ethylene diamine tetraacetic acid - EDTA) đã được thực hiện. Nghiên cứu, đánh giá cấu trúc tinh thể và hình thái học của vật liệu LiAlO2 sau khi chế tạo bằng kỹ thuật nhiễu xạ tia X (XRD) và kính hiển vi điện tử quét (SEM). Phân tích, đánh giá đường cong tích phân nhiệt phát quang của vật liệu LiAlO2 bằng phương pháp giải chập áp dụng các mô hình động học bậc 1, bậc 2 và bậc tổng quát. Vật liệu LiAlO2 có cấu trúc đơn pha gamma khi được nung ở nhiệt độ từ 900oC. Đường cong tích phân nhiệt phát quang của vật liệu LiAlO2 bao gồm hai đỉnh ở nhiệt độ 136 và 248oC, đỉnh 248oC được chọn làm đỉnh đo liều. Tinh thể γ-LiAlO2 đơn pha gamma được chế tạo thành công bằng phương pháp sol-gel kết hợp với EDTA. Điều kiện tối ưu để thu được tinh thể LiAlO2 đơn pha gamma là nhiệt độ thiêu từ 9000C trong thời gian 4 giờ với các hằng số mạng và tỷ trọng được xác định lần lượt là: a=5,16870 Å, c=6,26790 Å, và δ=2,615 g/cm³. Đường cong tích phân nhiệt phát quang của LiAlO2 được phân tích bằng phương pháp giải chập cho thấy sự phù hợp cao nhất với mô hình bậc tổng quát, với hệ số làm khớp FOM=1,08×10-2 và bậc động học b=1,79.synthesised LiAlO2 was studied for its structure and morphology by X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques. The thermoluminescence glow curve of LiAlO2 was analysed by deconvolution using the first-order, second-order, and general-order kinetic models. LiAlO2 material exhibits a single-phase gamma structure when calcined at temperatures starting from 900oC. The thermoluminescence glow curve of LiAlO2 consists of two peaks at 136 and 248oC, while peak 248oC is considered a dosimetric peak. The γ-LiAlO2 material was successfully synthesised using the sol-gel method combined with EDTA. The single-phase gamma LiAlO2 material was obtained after being sintered at temperatures greater than 900°C for 4 hours with lattice constants and density determined as follows: a=5.16870 Å, c=6.26790 Å, and δ=2.615 g/cm³. The thermoluminescence glow curve of LiAlO2 was analysed using the glow curve deconvolution method, which showed the best fit with the general-order model, with a fitting factor FOM=1.08×10-2 and a kinetic order b=1.79.

1. Đọc trực tuyến

1. Đọc trực tuyến

Tạo bộ sưu tập với mã QR