The luminescent nanomaterial YPO4:Tb was successfully synthesized using the combustion method. The crystal structure and optical properties were analyzed using X-ray diffraction (XRD), fluorescence excitation spectroscopy, emission spectroscopy, and lifetime measurements. The synthesized material was single-phase with a tetragonal crystal structure and an average particle size of 20 - 30 nm. Under 220 nm excitation, these materials exhibited strong blue emission corresponding to the 5D4 → 7FJ transitions of Tb3+, with the 5D4 → 7F5 transition being the most intense. The optimal synthesis temperature in laboratory conditions was from 800 to 900°C, with the best Tb3+ doping concentration at 7 mol%. The measured luminescence lifetime of the material was 363 μs.Vật liệu nano phát quang YPO4:Tb đã được tổng hợp thành công bằng phương pháp phản ứng nổ. Cấu trúc tinh thể và tính chất quang học được phân tích bằng nhiễu xạ tia X (XRD), quang phổ kích thích huỳnh quang, quang phổ phát xạ và phép đo thời gian sống. Vật liệu tổng hợp là đơn pha với cấu trúc tinh thể tetragonal và kích thước hạt trung bình từ 20 - 30 nm. Dưới ánh sáng kích thích 220 nm, vật liệu cho phát xạ màu xanh lam mạnh tương ứng với các chuyển đổi 5D4 → 7FJ của Tb3+, trong đó chuyển dời 5D4 → 7F5 là cường độ tốt nhất. Nhiệt độ tổng hợp tối ưu trong điều kiện phòng thí nghiệm là từ 800 đến 900°C, với nồng độ pha tạp Tb3+ tốt nhất là 7 mol%. Thời gian sống huỳnh quang đo được của vật liệu là 363 μs.