Carbon nanofibers (CNFs) materials are prepared via chemical vapor deposition (CVD) on Ni catalyst deposited on porous coal plates (C*), which were previously synthesized by the carbonization of coconut shells. The coal plates are used as support for preparing Ni/C* catalyst via three steps: impregnation of Ni2+, annealing, and reduction in a hydrogen flow. Morphology, structure, BET surface area, and porosity distribution of the CNF materials are characterized by X-ray Diffraction, Scanning Electron Microscope, and nitrogen isothermal adsorption-desorption. The produced CNFs material has homogeneous diameters (50 - 80 nm), a high surface area (207 - 224 m2/g), a pore volume (0.25 - 0.29 cm3/g), and a mass of 1.6 - 2.7 grams calculated by 1 gram of C* when the molar ratio of H2/LPG varied from 0.5 to 1.0.Vật liệu carbon nano sợi được tổng hợp trên xúc tác Ni phủ lên bề mặt tấm than xốp (C*) từ sọ dừa thải bằng phương pháp kết tụ hóa học từ pha hơi sử dụng khí dầu mỏ LPG làm nguồn carbon và hydro làm chất khử và chất pha loãng. Trong phương pháp này, than tổng hợp từ sọ dừa phế thải và dùng làm chất mang để phủ muối Ni2+ rồi nung và khử trong dòng khí H2 ở 450⁰C để tạo xúc tác Ni. Tính chất hóa lý của vật liệu như hình thái, cấu trúc và bề mặt riêng, phân bố lỗ xốp được xác định bằng các phương pháp như nhiễu xạ tia X (XRD), kính hiển vi điện tử quét (SEM) và hấp phụ - giải hấp đẳng nhiệt nitơ. Vật liệu CNF tạo thành có đường kính đồng đều từ 50 - 80 nm, bề mặt riêng và thể tích xốp cao (207 - 224 m2/g và 0,25 - 0,29 cm3/g), có khối lượng từ 1,6 - 2,7 gram tính trên 1 gram tấm than xốp khi thay đổi tỉ lệ mol H2/LPG từ 0,5 đến 1,0.