Ba1-xCaxTiO3 và các tính chất điện môi

• Ngôn ngữ: vie
• Ký hiệu phân loại: 621.35 Superconductivity
• Thông tin xuất bản: Communications in Physics, 2014
• Mô tả vật lý: 170-176
• Bộ sưu tập: Metadata
• ID: 505505

Tóm tắt

Ba1-xCaxTiO3 material samples with x changing from zero to 1 were fabricated by the solid state reaction method at a temperature of 1200°C in the ambient atmosphere. Crystalline structure of the material samples was recorded and identified by X-ray diffraction and Raman scattering. Analyzing the X-ray pattemsfound that Ba can be completely substituted by Ca with the concentration lower than 11 percent. The frequency dependence of the impedance (C) and AC conductance (G) of all the samples were recorded in a frequency range lower than 10 MHz by using an impedance analyzer HP 4192A. It was found that in the low frequency range lower than 1 MHz the dielectric constant and its loss decrease as Ca substituted for Ba. Besides an abnormal in the frequency dependence of the dielectric constant was observed for all samples in the higher frequency range up to 10 MHz.