Ảnh hưởng của thành phần nguyên liệu đến cấu trúc CeO2 dạng bông hoa chế tạo bằng phương pháp thủy nhiệt

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Mậu Chiến Đặng, Trung Dũng Đào, Đức Chánh Tín Đoàn, Ngọc Diệp Lê, Minh Tuệ Trần, Hoàn Phúc Từ

Ngôn ngữ: vie

Ký hiệu phân loại: 355.24 Raw materials

Thông tin xuất bản: Khoa học công nghệ Việt Nam, 2018

Mô tả vật lý: 45297

Bộ sưu tập: Metadata

ID: 534274

Thêm vào giỏ

Tóm tắt
Chủ đề

Bông hoa Ce(OH)CO3 với cẩu trúc ba chiều (3D) đã được chế tạo bằng phương pháp thủy nhiệt. Bông hoa chế tạo có các cánh hoa kích thước nano, lỗ rỗng sâu và thể tích lỗ rỗng lớn nên có diện tích bề mặt cao. Sau khi nung Ce(OH)CO3 ở 600°C trong không khí trong 6 giờ thu được CeO (Ceria) có cấu trúc giống bông hoa. Bông hoa CeO có cấu trúc dạng cầu đường kính 2-8 micromet, bên trong là các mao quản với bề dày các vách 20-30 nm. Hình dạng, kích thước và sự phân bố của các mao quản có thể được điều khiển bằng cách thay đổi thành phần nguyên liệu. Vật liệu mới này có thể được sử dụng làm chất xúc tác dựa trên nền Ceria cho phản ứng reforming khí metan tạo thành nhiên liệu khí hydro cho pin nhiên liệu. Bài báo này trình bày ảnh hưởng của các thành phần nguyên liệu trong quá trình thủy nhiệt lên bông hoa tạo thành.The Ce(OH)CO3 with three-dimensional (3D) flower structure has been prepared by the hydrothermal method. The collected flowers consisted of nano-sized petals and deep pores with the large pore volume, thus had high surface area. After calcining Ce(OH)CO3 at 600ºC in air for 6 hours, CeO2 (Ceria) were produced with a flowerlike structure. The CeO2 flowers had a spherical structure with a diameter of 2-8 micrometers, and the mesoporous structure inside of the microspheres had the walls of 20-30 nanometers. The shape, size, and distribution of the mesoporous could be controlled by changing the ingredient quantities. This new material can be used as a ceria-based catalyst for methane reforming to produce hydrogen for solid oxide fuel cells. This paper reports the effect of the ingredient quantities in the hydrothermal process on the formed CeO2 flowers.

Tạo bộ sưu tập với mã QR