Nghiên cứu phân bố độ bền kéo giữa các lớp in 3D kim loại theo phương pháp hàn đắp

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Tuấn Hưng Đồng, Sơn Minh Phạm

Ngôn ngữ: vie

Ký hiệu phân loại: 539.4 Modern physics

Thông tin xuất bản: Cơ khí Việt Nam, 2018

Mô tả vật lý: 21-25

Bộ sưu tập: Metadata

ID: 536502

Thêm vào giỏ

Tóm tắt
Chủ đề

In this study, the 3D rough drafted metal workpiece was created by MAG welding method, combining CNC milling machine, with the same welding parameters but different welding directions: "Direction parallel to the welding line", "Direction tangent to welding line ". Samples were created according to TCVN 197, using destructive methods at room temperature. Experimental results show that the strength decreases from high to low in the order: "Direction parallel to the welding line" to "The right angle welding line" is the "Direction tangent to the welding line". High durability in areas with concentrated material density: The middle layer is higher than the outside
the lower layer is higher than the upper layer.Trong nghiên cứu này, phôi thô thử kéo in 3D kim loại được tạo bằng phương pháp hàn đắp - MAG, kết hợp máy phay CNC, với cùng thông số hàn nhưng khác hướng hàn: "Hướng song song với đường hàn", "Hướng tiếp tuyến với đường hàn". Mẫu được tạo theo TCVN 197, sử dụng phương pháp phá hủy ở nhiệt độ phòng. Kết quả thực nghiệm cho thấy độ bền giảm từ cao đến thấp theo thứ tự: "Hướng song song với đường hàn" đến "Hướng vuông góc đường hàn" cuối cùng là "Hướng tiếp tuyến với đường hàn". Độ bền cao tại những vùng có mật độ vật liệu tập trung: Lớp giữa cao hơn so với bên ngoài
lớp dưới cao hơn lớp bên trên.