Polyethylene terephthalate (PET) is a semi-crystalline polymer that finds broad use. Consequently, it contributes to the accumulation of plastics in the environment, warranting PET recycling technologies. Ball milling is a commonly used technique for the micronization of plastics before transformation. It has also recently been reported as an efficient mixing strategy for the enzymatic hydrolysis of plastics in moist-solid mixtures. However, the effect of milling on the microstructure of PET has not been systematically investigated. Thus, the primary objective of this study is to characterize the changes to the PET microstructure caused by various ball milling conditions. PET of different forms was examined, including pre- and post-consumer PET, as well as textiles. The material was treated to a range of milling frequencies and duration, before analysis of particle size, crystallinity by differential scanning calorimetry and powder X-ray diffraction, and morphology by scanning electron microscopy. Interestingly, our results suggest the convergence of crystallinity to ~30 % within 15 minutes of milling at 30 Hz. These results are consistent with an equilibrium between amorphous and crystalline regions of the polymer being established during ball milling. The combined data constitutes a reference guide for PET milling and recycling research.