OBJECTIVES: Evaluated the effect of phosphorylated chitosan (ChiPh) and nano-sized sodium trimetaphosphate (TMPnano) incorporation into resin modified glass ionomer cement (RMGIC) on mechanical, fluoride release, antimicrobial and cytotoxic properties. METHODS: RMGIC was combined with ChiPh (0.25 %/0.5 %) and/or TMPnano (14 %). The diametral compressive/tensile strength (DCS/TS), surface hardness (SH) and degree of conversion (%DC) were determined. For fluoride (F) release, samples were immersed in DE/RE solutions. Antimicrobial/antibiofilm activity was evaluated by agar diffusion test/biofilm metabolism. Cytotoxicity on MDPC-23 odontoblast cell lines was evaluated. RESULTS: TS and DCS (24 h), all the groups were similar (p >
0.05). After 7 days, RMGIC-14 %TMPnano-0.25 %ChiPh showed the best results for TS/DCS (p <
0.05). The SH was lower and similar for the RMGIC and RMGI-14 %TMPnano-0.5 %ChiPh groups (p >
0.05) after 24 h
after 7 days, all groups containing TMPnano and/or ChiPh showed higher SH when compared to RMGIC, except for RMGIC-0.5 % ChiPh. The %DC was similar for all groups (p = 0.172). There was a gradual release of F for all groups during the 15 days
in the cumulative analysis, after 15 days, the RMGIC-14 %TMPnano-0.25 %ChiPh group showed the highest value (p <
0.05). Viability against S. mutans was observed for the RMGIC-14 %TMPnano-0.25 %ChiPh group (p <
0.05). After 24 h, the RMGIC-0.25 %ChiPh and RMGIC-14 %TMPnano-0.25 %ChiPh groups showed the lowest cytotoxic effect (p = 0.371)
at 48 h/72 h, only the RMGIC-14 %TMPnano-0.25 %ChiPh group showed similar cytocompatibility. CONCLUSION: The addition of ChiPh (0.25 %) and TMPnano (14 %) improved the RMGIC's mechanical, antimicrobial/antibiofilm and cytotoxic properties. CLINICAL RELEVANCE: ChiPh and TMPnano into RMGIC could be a promising restorative material for application in patients with active dental caries.