To investigate the dynamic characteristics, energy dissipation patterns, and failure modes of granite with filled joints of varying thicknesses under impact loading, we utilized the Split Hopkinson Pressure Bar (SHPB) test setup for impact tests on both unfilled and filled granite samples. Additionally, a high-speed camera was used to capture the dynamic failure and crack propagation processes of the rock samples in real time. The results indicate that the thickness of the filling material significantly affects the stress-strain behavior of jointed rock masses, particularly in terms of characteristics of stress variation and post-peak morphology. In comparison to unfilled jointed rock samples, a distinct "stress bimodal" phenomenon is present, and the rebound of strain following the peak gradually decreases. The fracture patterns observed in the jointed rock samples are primarily characterized by tensile failure. Damage is notably more pronounced on the left side of the samples (near the incident bar), the lower side, and in the areas filled with gypsum. The most severe degree of damage occurs when the filling thickness is 7.56 mm. As the thickness of the filling increases, the dynamic compressive strength of the rock mass diminishes, and the peak strain first increases and then decreases. Concurrently, the energy reflection coefficient of the rock mass increases linearly, while the energy transmission coefficient declines linearly. Furthermore, the energy dissipation ratio first increases and then decreases. The test data reveal that the critical filling thickness influencing the dynamic properties, energy absorption characteristics, and damage degree of jointed rock samples falls within 4.91 mm to 7.56 mm.