In this paper, regression and re-aging treatment (RRA) was performed on the 7050 alloy, and the evolution in the microstructure of the 7050 alloy was observed by metallography and SEM. The effect of regression and re-aging treatment on the hardness of the alloy was investigated
the maximum hardness was 84.576 HRB at 180 °C/30 min. It was found that with the increase in regression treatment time, the size of the precipitates on the grain boundaries gradually increased, while the number of the precipitates inside the grain decreased accordingly. In the course of the experiment, the η' (MgZn