OBJECTIVES: This study aims to characterize a three-dimensional-printed hydroxyapatite (HA)/polycaprolactone (PCL) scaffold and assess its biocompatibility both METHODS: A bionic, porous HA/PCL scaffold was fabricated using 3D printing, and its microstructure, porosity, hydrophilicity, and mechanical properties were evaluated through scanning electron microscopy and various assays. Bone marrow mesenchymal stem cells (BMSCs) and vascular endothelial progenitor cells (VEPCs) were co-cultured with the scaffold, and their proliferation and osteogenic differentiation were assessed using the Cell Counting Kit-8, ALP assays, and alizarin red staining. Osteogenic marker expression was analyzed via qRT-PCR. RESULTS: The average pore size of the scaffold was 462.00 ± 100.389 μm, with a porosity of 53%, a water absorption expansion rate of 5.10%, a contact angle of 94.55°, an elastic modulus of 53.82 MPa, and a compressive strength of 6.10 MPa. ALP activity and qRT-PCR analysis of osteogenic markers (BMP2, OCN, Runx2) showed significant upregulation in cells co-cultured with the scaffolds. In vivo experiments demonstrated enhanced bone regeneration and collagen deposition in the HA/PCL scaffold group. CONCLUSION: The results suggest that the HA/PCL scaffold promotes osteogenic differentiation and bone regeneration, making it suitable for bone tissue engineering applications.