Mechanical Properties and Strengthening Contributions of AISI 316 LN Austenitic Stainless Steel Grade.

0 Người đánh giá. Xếp hạng trung bình 0

Tác giả: Jana Bidulská, Róbert Bidulský, Alica Fedoríková, Tibor Kvackaj

Ngôn ngữ: eng

Ký hiệu phân loại: 133.5273 Astrology

Thông tin xuất bản: Switzerland : Materials (Basel, Switzerland) , 2025

Mô tả vật lý:

Bộ sưu tập: NCBI

ID: 77027

Thêm vào giỏ Liên kết toàn văn

The main goal of this contribution is to evaluate the mechanical properties, strengthening contributions and microstructure development of austenitic stainless steel AISI 316 LN with high nitrogen content in the states characterized as the initial state and the states after rolling with different thickness deformations. The initial state was represented by solution annealing (777 K/60 min). The deformation state was characterized by rolling thickness reductions carried out at ambient temperature (