The study aims to assess the effect of printing orientation on surface roughness and gloss of resins for 3D printing of aligners. Squared specimens (14 × 14 × 4 mm) were printed using Dental LT Clear (Formlabs, Somerville, MA, USA
LT) or Tera Harz TC-85 DAC (Graphy, Seoul, Republic of Korea
TC) with different orientations: 0° (horizontal), 90° (vertical), and as per the manufacturer's recommendation (40° for LT, 60° for TC). A profilometer was used to measure roughness (Ra) in µm, while gloss was recorded in gloss units (GU) with a glossmeter. The collected data were statistically analyzed. Material type did not significantly influence roughness, while print orientation was an influential factor, with the orientation recommended by the manufacturer yielding the roughest specimens. Vertical printing resulted in significantly higher roughness than horizontal. Material type was a significant factor for gloss, with TC exhibiting significantly higher gloss than LT. Print direction significantly influenced gloss, with vertical printing resulting in the highest gloss. The finding of higher roughness for vertical prints can be explained by the presence of a greater number of layers. The superior gloss exhibited by TC regardless of print angulation could be related to the effective cleaning of uncured resin by centrifugation and to the high degree of monomer conversion in nitrogen atmosphere.