The aim of this work was to assess the influence of the parameters of the hot isostatic pressing (HIP) process and the direction of printing of Ti-6Al-4V samples made using the laser-engineered net shaping (LENS) method on strength properties. The tests were carried out using a static testing machine and a digital image correlation system. Samples before and after the HIP process were tested. The HIP process was carried out at a temperature of 1150 °C, a heating time of 240 min and various pressure values of 500, 1000 and 1500 bar. Based on the comparative analysis of the test results, it has been shown that the ability to adjust the parameters of the HIP process has a significant impact on the final mechanical properties of the samples.